This reports the electrical properties of single-crystal β-gallium oxide (β-Ga₂O₃) vertical Schottky barrier diodes (SBDs) with a different guard ring structure. The vertical Schottky barrier diodes (V-SBDs) were fabricated with two types guard ring structures, one is with metal deposited on the Al₂O₃ passivation layer (film guard ring: FGR) and the other is with vias formed in the Al₂O₃ passivation layer to allow the metal to contact the Ga₂O₃ surface (metal guard ring: MGR). The forward current values of FGR and MGR V-SBD are 955 mA and 666 mA at 9 V, respectively, and the specific on-resistance (Ron,sp) is 5.9 mΩ·cm² and 29 mΩ·cm². The series resistance (Rs) in the nonlinear section extracted using Cheung’s formula was 6 Ω, 4.8 Ω for FGR V-SBD, 10.7 Ω, 6.7 Ω for MGR V-SBD, respectively, and the breakdown voltage was 528 V for FGR V-SBD and 358 V for MGR V-SBD. Degradation of electrical characteristics of the MGR V-SBD can be attributed to the increased reverse leakage current caused by the guard ring structure, and it is expected that the electrical performance can be improved by preventing premature leakage current when an appropriate reverse voltage is applied to the guard ring area. On the other hand, FGR V-SBD shows overall better electrical properties than MGR V-SBD because Al₂O₃ was widely deposited on the Ga₂O₃ surface, which prevent leakage current on the Ga₂O₃ surface.