In this study, we fabricated single grain YBCO bulk superconductors with control of the distance between the seed and the upper surface of the YBCO compacts. The magnetic levitation force of the YBa₂Cu₃O₇ superconducting bulk, which corresponds to the energy amount of the superconducting bulk, was measured to be 32.634 N at the center of the bulk where the seed was placed. Under field cooling conditions, a capture magnetic force of 2.17 kG was observed at the center of the bulk. The trapped magnetic force curve corresponding to the stability of the superconducting bulk means that the superconducting specimens were well grown in the form of single grains.

To improve superconductor properties, the size of the crystal grains of the superconductor should be adjusted, the amount of electricity flowing through the superconductor should be increased, and the superconductor should be designed to withstand external magnetic fields. It is necessary to control the microstructure so that many flux pinning centers are developed inside the superconductor so that defects are generated physically or chemically, and the micro secondary phase for trapped magnetic flux must be dispersed inside the superconductor. In order to measure the superconducting magnetic force of the superconducting bulk in a simplified manner, the superconducting magnetic force was analyzed using an Nd-Fe-B permanent magnet of 3.80 kG. In particular, by delaying the growth of partially melted Y₂BaCuO₅ particles, we devised a plan to refine Y₂BaCuO₅ particles to effectively improve superconducting magnetic force, and analyzed superconducting magnetic force in a single crystal YBa₂Cu₃O_7-y superconducting bulk using a gauss meter. The melted superconducting bulk traps 80% or more of the applied magnetic field, and can be used as a bulk magnet of high magnetic field magnetization applicable to electric power equipment.

This aim of this study was to develop a process for creating bulk single-crystal YBaCuO superconductors in a high magnetic field. To support the bulk unidirectional growth of YBa₂Cu₃O_7-y, SmBa₂Cu₃O_7-y seeds were planted inside YBaCuO composites and samples were produced by melting, enabling the growth of two YBaCuO superconductors. Due to the magnetism generated inside the superconductor of the upper sample, the magnetization inside the superconducting single crystals was evenly distributed, the sharpness of the induced magnetic force was improved, and the superconducting magnetization were significantly improved. This approach is widely applicable for the production of superconducting wires and current leads used for DC power breakers.