In the (La0.8Ca0.2)(Cr0.9Co0.1)O3 (LCCC), which has been using as interconnector materials in SOFC, Al ions were substituted for Co because ionic radius of Al is similar to that of Co. Because of the almost identical ionic radius of Al and Co, the substitution was not thought to be affect the tolerance factor of LCCC, and the densification behavior, high temperature electrical conductivity and thermal expansion coefficient were examined as a function of Al concentration. In the cases of the x= 0 and x= 0.02 in (La0.8Ca0.2)(Cr0.9Co0.1-xAlx)O3 (x= 0∼0.1), the samples showed the relative densities above ≥95% when those were sintered at ≥1,350℃. In the case of the x≥0.06 the sintered density deteriorated greatly at lower sintering temperatures. High temperature electrical conductivity of the samples decreased as the content of Al increased. Since the valence state of Al ion is unchangeable, while Cr or Co ions contribute to the electrical conduction by changing those valence states, Al substitution resulted in the decreased electrical conductivity. Al doping of LCCC was an effective way of decreasing the thermal expansion coefficient (TEC).
Maintenance Priority Index of Overhead Transmission Lines for Reliability Centered Approach Jae-Haeng Heo, Mun-Kyeom Kim, Dam Kim, Jae-Kun Lyu, Yong-Cheol Kang, Jong-Keun Park Journal of Electrical Engineering and Technology.2014; 9(4): 1248. CrossRef
First
Prev