In this study, in order to develop the capacitor composition ceramics with the good dielectric properties, (Ba1-xCax)(Ti0.85Zr0.12Sn0.03)O3 (abbreviated as BCTZ) ceramics were prepared by the conventional solid-state reaction method. The effects of Ca substitution on the microstructure and dielectric properties was investigated. The X-ray diffraction patterns demonstrated that all the specimens showed perovskitephase, and secondary phases are indicated in the measurement range of X-ray diffraction. Also, all the specimens indicated an rhombohedron phase structure. It was identified from the X-ray diffraction patterns that the secondary phase formed in grain boundaries and then decreased the dielectric properties. For all the specimens, observed one peak was tetragonal cubic phase transition temperature(TC),which is located in the vicinity of room temperature.