We investigated the characterizations of carbon films fabricated by dual magnetron sputtering under various film thickness for the electrodes in TCO-less DSSC (dye-sensitized solar cells). Carbon films prepared at various conditions were exhibited smooth and uniform surfaces without defects. Also, the rms surface roughness of carbon films was decreased from 2.25 nm to 1.0 nm with the increase of film thickness. The sheet resistance as the electrical properties are improved from 11.2×10-3 to 2.28×10-3 with the increase of film thickness. In the results, the performance of TCO-less DSSC critically depended on the film thickness of working electrodes, indicating the conductivity of carbon films.