Modern thin film deposition processes require high deposition rates, low costs, and high-quality films. Atmospheric pressure plasma-enhanced chemical vapor deposition (AP-PECVD) meets these requirements. AP-PECVD causes little damage on thin film deposition surfaces compared to conventional PECVD. Moreover, a higher deposition rate is expected due to the surface heating effect of atomic hydrogens in AP-PECVD. In this study, polycrystalline silicon thin film was deposited at a low temperature of 100℃ and then AP-PECVD experiments were performed with various plasma powers and hydrogen gas flow rates. A deposition rate of 15.2 nm/s was obtained at the VHF power of 400 W. In addition, a metal foam showerhead was employed for uniform gas supply, which provided a significant improvement in the thickness uniformity.

In this paper, experimental analyses have been performed to compare the electrical characteristics of n channel LT(low temperature) and HT(high temperature) poly-Si TFTs(polycrystalline silicon thin film transistors) on quartz substrate according to activated step annealing. The size of the particles step annealed at low temperature are bigger than high temperature poly-Si TFTs and measurements show that the electric characteristics those are transconductance, threshold voltage, electric effective mobility, on and off current of step annealed at LT poly-Si TFTs are high more than HT poly-Si TFT`s. Especially we can estimated the defect in the activated grade poly crystalline silicon and the grain boundary of LT poly-Si TFT have more high than HT poly-Si TFT`s due to high off electric current. Even though the size of particles of step annealed at low temperature, the electrical characteristics of LT poly-Si TFTs were investigated deterioration phenomena that is decrease on/off current ratio depend on high off current due to defects in active silicon layer.

Analyzing electrical degradation of polycrystalline silicon transistor to applicable at several environment is very important issue. In this research, after fabricating p channel poly crystalline silicon TFT (thin film transistor) electrical characteristics were compare and analized that changed by gate bias with first measurement. As a result on and off current was reduced by variation of gate bias and especially re duce ratio of off current was reduced by 7.1×101. On/off current ratio, threshold voltage and electron mobility increased. Also, when channel length gets shorter on/off current ratio was increased more and thresh old voltage increased less. It was cause due to electron trap and de-trap to gate silicon oxide by variation of gate bias.

To integrate the sensor driver and logic circuits, fabricating down scaled transistors has been main issue. At this research, short channel effects were analyzed after n channel polycrystalline silicon thin film transistor was fabricated at high temperature. As a result, on current, on/off current ratio and transconductance were increased but threshold voltage, electron mobility and s-slope were reduced with a decrease of channel length. When carriers that develop at grain boundary in activated polycrystalline silicon have no gate biased, on current was increased with punch through by drain current. Also, due to BJT effect (parallel bipolar effect) that developed under region of channel by increase of gate voltage on current was rapidly increased.