We have studied the thermal stability of NCM622 cathode material for Li-ion batteries using real-time synchrotron x-ray scattering below 600°C in both air and vacuum. The expansion of the mean particle size, which reached maximum values of 10.3 μm in air and 10.6 μm in vacuum at 200°C, was attributed to the dehydration of intergranular water within the NCM622 powders. Across all annealing temperatures, the amount of crystal NCM622 phase in air was consistently higher than that in vacuum. The crystal domain sizes in air showed less variation than that in vacuum during annealing from RT to 500°C. These indicate that the crystal NCM622 phase is more thermally stable during annealing in air than in vacuum. This stability is attributed to the presence of 21% oxygen in air, which is absent under vacuum conditions.

We have studied the effects of Ag on the characteristics of Sn₄₈In₅₂Ag_x (wt%) low-melting solders for photovoltaic ribbons. The Sn₄₈In₅₂ (wt%) solder coexisted in the InSn₄ and In₃Sn alloys. Ag atoms added in the solder formed an AgIn₂ alloy by reacting with some part of In atoms, while they did not react with Sn atoms. The addition of Ag atoms in the Sn₄₈In52Agx (wt%) solders showed useful results; an increase in peel strength and a decrease in melting temperature. The peel strength of the ribbon plated with the Sn⁴⁸In⁵² (wt%) solder was 53.6 N/mm², and that of the Sn⁴⁸In⁵²Ag1 (wt%) solder largely increased to 125.1 N/mm². In the meanwhile, the melting temperature of the Sn₄₈In⁵² (wt%) solder was 119.2℃, and that of the Sn48In52Ag1 (wt%) solder decreased to 114.0℃.

We studied the various characteristics of Sn-In (wt%) Pb-free solders for photovoltaic ribbon application. The solders near the eutectic composition of Sn₄₈In₅₂ (wt%) existed in InSn₄ and In₃Sn alloy phases, and in In crystal phase, but not in Sn crystal phase. In addition, the InSn4 phase (γ-alloy) existed separately from the In₃Sn (β-alloy) and the In phase confirmed by an SEM-EDS-mapping. The melting temperature of the eutectic solder of Sn₄₈In₅₂ (wt%) was 119.2℃, and when the Sn content decreased in reference to the eutectic composition, it slightly increased to 121.4℃, but when the Sn content increased, it remained almost constant at 119.1℃. The peel strength of the ribbon plated with the Sn₄₂In₅₈ (wt%) solder was 38.7 N/㎟, and it tended to increase when the Sn content increased. The peel strength of the eutectic Sn₄₈In₅₂ (wt%) solder was 53.6 N/㎟, and that of the Sn₅₁In₄₉ (wt%) solder was 61.6 N/㎟ that was the highest.