We investigated the dielectric relaxation properties 0.5Ba(Zr0.2Ti0.8)O3-0.5(Ba0.7Ca0.3)TiO3 ceramics with CuO addition. With increasing CuO addition, the lattice parameter was increased by substitution of small amount Cu2+ ion in B-site of 0.5Ba(Zr0.2Ti0.8)O3-0.5(Ba0.7Ca0.3)TiO3 ceramics. Also the grain size and the maximum dielectric constant of 0.5Ba(Zr0.2Ti0.8)O3-0.5(Ba0.7Ca0.3)TiO3 ceramics was decreased with increasing amounts of CuO addition. Moreover, the diffused phase transition properties (γ) of 0.5Ba(Zr0.2Ti0.8)O3-0.5(Ba0.7Ca0.3)TiO3 ceramics was increased by compositional fluctuation with increasing of CuO amount, changed from 1.45 at 1 wt% CuO addition to 1.94 at 7 wt% CuO addition.