In this study, (1-x)Pb(Mg1/2W1/2)0.03(Ni1/3Nb2/3)0.09(Zr0.5Ti0.5)0.88O3 + xCeMnO3 (x= 0∼0.02) ceramics were prepared by Columbite precursor method. The phase structure, ferroelectric and piezoelectric properties were systematically investigated. It was found that PMW-PNN-PZT possessed superior electrical properties due to its composition close to the MPB (morphotropic phase boundary). Coercive electric field of 10.05 [kV/cm] and density of 7.88 [g/cm3] were obtained when the substitution amount of CeMnO3 is x=0.02. In contrast, specimens with x=0.01 showed the mechanical quality factor(Qm) of 1,091 and the electromechanical coupling factor(kp) of 0.613.