We report the studies on the red organic phosphor by using perylene bisimide derivatives. Even though perylene bisimide derivatives have excellent thermal stability and luminous efficiency, they have low solubility in organic solvents. In this research, modified perylene bisimide derivative, N,N`-Bis(4-bromo-2, 6-diisopropylphenyl)- 1, 6, 7, 12-tetraphenoxyperylene-3, 4, 9, 10-tetracarboxyl bisimide (1C), has been prepared by the reaction of phenol with N,N`-Bis(4-bromo-2, 6-diisopropylphenyl)-1, 6, 7, 12-tetrachloroperylene-3, 4, 9, 10-tetracarboxyl bisimide (1B) in presence of DMF, at 70℃. The synthesized (1C) was characterized by using 1H-NMR, FT-IR, UV/V is spectroscopy, and TGA. The absorbtion and emission of (1C) was shown at 576 nm and 610 nm in UV/V is spectrum. In TGA thermogram, (1C) showed good thermal stability without significant weight loss to 220℃. And in the solubility analysis, (1C) with phenoxy group showed the good solubility in general organic solvents. The blended films of (1C) with PMMA (polymethyl methacrylate) at different weight % concentration such as 10, 5, 1 weight % have been prepared. The blended film was shown at 616 nm when monitored at 450 nm in PL emission spectra.