In this study, SiO2 20 phr, ATH 70 phr, and platinum flame retardant were mixed with raw silicone rubber and -10 kV was applied to measure electrostatic charge attenuation voltage, surface resistance, and volume resistance, and the following conclusions were obtained. When the platinum flame retardant was 0 phr, the humidity 74.6% and the temperature was 21.8℃, the potential was half-reduced to 0.63 kV, 0.57 kV, and 0.44 kV when the applied voltage was changed from -10 kV to -8 kV, and the time halved to 50% was increased to 2.40 seconds, 2.47 seconds, and 2.61 seconds. It was confirmed that as the platinum flame retardant increased from 0.1 to 0.3 phr, the potential half-reduced to 0.67 kV, 0.60 kV, and 0.595 kV decreased, and the charge potential attenuation time half-reduced to 50% decreased to 3.44 seconds, 1.78 seconds, and 1.60 seconds. It was confirmed that the surface resistance increased as the humidity decreased, and the volume resistance decreased as the platinum flame retardant increased.