In this study, the electrical properties of a C0G (class 1 ceramic) dielectric composition with internal reducibility, specifically (Ba0.27CaSr)(Zr0.95Ti0.05)O₃, were investigated by fixing Ba at the A site and varying the Ca/Sr molar ratio. The potential application of this composition in high-permittivity C0G MLCCs was examined. The powder was calcined at 1,150℃ for 2 hours, as determined by TG-DTA analysis, and the resulting powder was ground to achieve a particle size (D50) of 0.35 to 0.4 μm and a specific surface area (BET) of 4.5 to 5.0 g/m². With a Ca/Sr molar ratio of 0.3, the composition (Ba0.27Ca0.17Sr0.56) (Zr0.95Ti0.05)O₃ exhibited electrical properties with a permittivity of 41.9, a loss of less than 0.008%, and an insulation resistance exceeding 2.2×10¹³ Ω. The feasibility of using this composition for high-capacitance C0G MLCCs was confirmed.