In this work, in order to develop the ceramics with an excellent electrocaloric effect, [Bi0.5(Na0.84K0.16)0.5]TiO3 ceramics were fabricated by conventional solid state reaction method. The ceramics was observed as rhombohedral phase by X-ray diffraction patterns. To investigate the electrocaloric effect of the ceramics, P-E hysteresis loops were measured at various temperature. The temperature change ΔT of these ceramics was calculated using the Maxwell``s relations. The maximum value of temperature change ΔT was obtained as 0.3 1℃ at 165℃ under applied electric fields 45 kV/cm.